Тезис
This document specifies a method for the determination of the particle size distribution of coating powders by sieve analysis. Particle size distributions with a maximum of less than 100 µm is determined by laser diffraction, ISO 8130‑13. This method is used especially for determining the oversize material or for the presence of contamination and can be used as a quality control procedure ("go"/"no go" test) by checking the amount retained on a single sieve.
The following particle sizes are typical for coating powders, however the particle size can deviate depending on the application:
— thin-film technology: 1 µm to 63 µm;
— electrostatic coating: 10 µm to 200 µm;
— fluidizing-bed method: 100 µm and above.
NOTE Sieves with a mesh size smaller than 32 µm are not practical and are likely to become blind during use.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 2019-04Этап: Систематический пересмотр международного стандарта [90.20]
-
Версия: 2
-
Технический комитет :ISO/TC 35/SC 9ICS :87.040
- RSS обновления
Жизненный цикл
-
Ранее
ОтозваноISO 8130-1:1992
-
Сейчас
ОпубликованоISO 8130-1:2019
Стандарт, который пересматривается каждые 5 лет
Этап: 90.20 (Hа стадии пересмотра)-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
Появились вопросы?
Ознакомьтесь с FAQ
Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)